Name: SiSiB® LR1360
Brand: Nanjing SiSiB Silicones Co., Ltd.
Price: 100 USD

Technical Data

Color	Transparent
Viscosity A (mPa·s)	850,000-1,000,000
Viscosity B (mPa·s )	750,000-900,000
Hardness (Shore A)	58-60
Tensile Strength (MPa)	Min.7.0
Elongation (%)	Min.400
Tensile Set (%)	Max.5.0
Tear Strength (kN/m)	Min.30
Linear shrinkage (%)	1.6-2.5

Curing Conditions

Typical cure: 140°C × 10 minutes

Post cure: 200°C × 4 hours (recommended for optimal mechanical stability)

Actual curing time depends on mold temperature and part thickness.

Above values are typical data and should not be used as specification.

Application

Platinum-catalyzed curing materials for medical devices and accessories.

Component A and B enter the mixer of the injection machine in a 1:1 ratio through metering and mixing equipment, and are then directly injected into the mold that has been preheated to 100°C to 160°C. After a few seconds, the cured elastomer is obtained.

SiSiB® LR1360 is designed for high-transparency, high-elasticity molded parts used in medical and protective applications. It offers reliable mechanical performance and long-term stability under demanding conditions. Typical applications include:

Silicone masks
Medical device accessories
Respiratory components
Transparent molded parts

Packing and Storage

SiSiB® LR1360 is supplied in 20Kg plastic drum, 200Kg steel drum.

This document does not contain the product safety information required for safe use. Before handling, please refer to the product and safety data sheets, as well as container labels, for information on safe usage, physical hazards, and health risks. Safety Data Sheet is available on the website, from the distributor, or by contacting SiSiB customer service.

Documents

SiSiB® LR1360 Safety Data Sheet

Products

Blog

Cancellation of China Export VAT Rebate for Certain Products
Jan 12 , 2026

LSR for Mask

Technical Data

Application

Packing and Storage

Documents